Usage
Appliance Paint, Boat Paint, Building Coating, Car Paint, Paper Coating, Plastic Coating, back side solar cell paste Viscosity (NDJ-8S, #4, 25±0.5℃)
Drying1
Chain fast burning furnace: 280℃-350℃/25-50sec Drying2
Rotating drying furnace: 180℃-250℃/8-15min Practical Peak Temperature
Wet Deposit (g/pcs) (156*156)
Resistivity (Fired Thickness)
Adhesion (N)
>20 (Single side EVA tape) Cell Warpage (156 silicon,180μm)
Monocrystal silicon: ≤2.0mm; Polysilicon:≤1.8mm